Структура, ионная проводимость и термодинамика новых соединений на основе оксидов висмута и рения

Show simple item record

dc.contributor.author Мацкевич, Н. И.
dc.contributor.author Брызгалова, А. Н.
dc.contributor.author Wolf, Th.
dc.contributor.author Greaves, C.
dc.contributor.author Наумов, В. Н.
dc.contributor.author Вязовкин, И. В.
dc.contributor.author Чупахина, Т. И.
dc.date.accessioned 2014-12-12T20:02:01Z
dc.date.available 2014-12-12T20:02:01Z
dc.date.issued 2012
dc.identifier.citation Мацкевич Н. И. [и др.] Структура, ионная проводимость и термодинамика новых соединений на основе оксидов висмута и рения // Вестник НГУ. Серия: Физика. – 2012. – Т. 7. – Вып. 3. – С. 122-128. – ISSN 1818-7994. ru_RU
dc.identifier.issn 1818-7994
dc.identifier.uri https://lib.nsu.ru/xmlui/handle/nsu/4006
dc.description.abstract Методом твердофазных реакций из оксида висмута (Bi2O3), перрената аммония (NH4ReO4), оксида лютеция (Lu2O3) и оксида гольмия (Ho2O3) синтезированы соединения Bi14ReO24.5, Bi12.5Lu1.5 ReO24.5, Bi12.5Ho1.5 ReO24.5. Методом рентгеноструктурного анализа определены параметры решетки и пространственная группа. Соединение Bi14ReO24.5 имеет тетрагональную симметрию, пространственная группа I 4/m, а соединенияBi12.5Ho1.5ReO24.5 и Bi12.5Lu1.5ReO24.5 – кубическую симметрию, пространственная группаFm3m. Методом импеданс-спектроскопии измерена ионная проводимость фазыBi12.5Lu1.5ReO24.5 в интервале температур500–900 ºС. Показано, что Bi12.5Lu12.5ReO24.5является одним из перспективных ионных проводников в области средних температур и имеет проводимость при800 К такую же, как BiCuVOx, Bi12.5Ln12.5 ReO24.5(Ln = La, Nd). Методом калориметрии растворения в соляной кислоте концентрацией 2 моль•л–1(2 М) измерена теплота растворенияBi12.5Lu1.5ReO24.5. С использованием полученных и литературных данных оценена теплота образования из бинарных оксидов и показано, что соединениеBi12.5Lu1.5ReO24.5является термодинамически устойчивым при комнатных температурах. ru_RU
dc.description.abstract New compounds Bi14ReO24.5, Bi12.5Lu1.5ReO24.5, Bi12.5Ho1.5ReO24.5were synthesized by solid-state method with bismuth oxide, Bi2O3, ammonium perrhenate, NH4ReO4, lutecium oxide, Lu2O3, and holmium oxide, Ho2O3. The lattice parameters and space group were determined by X-ray diffraction spectroscopy. Bi14ReO24.5 has tetrahedral symmetry, space group I 4/m, Bi12.5Ho1.5ReO24.5иBi12.5Lu1.5ReO24.5 have cubic symmetry, space group Fm3m. Ionic conduction of Bi12.5Lu1.5ReO24.5phase was measured by impedance spectroscopy in a temperature range from 500 to 900 °C. It was shown Bi12.5Lu12.5ReO24.5is one of the best ionic conductors in range of medium temperatures and has the same conductivity as that for BiCuVOx, Bi12.5Ln12.5ReO24.5(Ln = La, Nd) at 800 K. The heat of solution for Bi12.5Lu1.5ReO24.5was measured by solution calorimetry in hydrochloric acid with concentration 2 mol*L-1(2M). The heat of formation from binary oxides was estimated using finding and literary data; it was shown Bi12.5Lu1.5ReO24.5 is thermodynamically stable at room temperatures. ru_RU
dc.description.sponsorship Работа выполнена при финансовой поддержке Института физики твердого тела (Карлсруэ Институт технологий, Германия) и Программы фундаментальных исследований СО РАН. ru_RU
dc.language.iso ru ru_RU
dc.publisher Новосибирский государственный университет ru_RU
dc.subject оксид висмута ru_RU
dc.subject Bi2O3 ru_RU
dc.subject калориметрия растворения ru_RU
dc.subject стабильность ru_RU
dc.title Структура, ионная проводимость и термодинамика новых соединений на основе оксидов висмута и рения ru_RU
dc.title.alternative Structure, ionic conduction and thermodynamics of new compounds based on bismuth and renium oxides ru_RU
dc.type Article ru_RU