The present paper describes the possibility of strong porous ceramics preparation from hydroxyapatite nanopowders. The as-dried hydroxyapatite nanopowders were uniaxially compacted and sintered. The sintered ceramics and nanopowders were analyzed by methods of transition electron microscopy, scanning electron microscopy and X-ray phase diffraction. The ceramics gas-penetration and hardness were measured. The methods of pore control were tested. The ceramics samples with open equally dispersed pores were received; the pores and grain size is about micron and less. The results are useful for making medical implantate and membrane ceramics with controlled pores size.
Проведены исследования по получению керамики из наноразмерного порошка гидроксиапатита путем «сухого» одноосного прессования и последующего спекания. Исходный порошок и керамику изучали методами просвечивающей и сканирующей электронной микроскопии, рентгенофазового анализа. Измерены их свойства, в частности микротвердость структуры керамики. Получены прочные керамические образцы с равномерно распределенной по объему открытой пористостью с размером зерен и пор порядка микрона и менее. Полученные результаты могут быть полезны при создании медицинских имплантатов на основе гидроксиапатита и керамических мембран с контролируемой пористостью.